Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.
Scientific Reports volume 13, Article number: 15627 (2023 ) Cite this article 3000f Supercapacitor
Graphene presents practical applications in energy storage devices, especially supercapacitors. However, mainstream synthesis of graphene includes toxic chemical usage, which threatens the environment. With the recent attention shift to synthesizing nanomaterials from agro-waste due to their easy availability, cost-effectiveness, and, most importantly, their environmental friendliness, we present, in this work for the first time, a novel and green synthesis of few-layered graphene sheets using pomegranate peels as a precursor at a low temperature of 80 °C. The surface morphology and microstructural properties are determined by Transmission Electron Microscopy (TEM), Energy Dispersive X-Ray spectroscopy (EDX), X-Ray Diffraction (XRD), Fourier Transform Infrared Spectroscopy (FTIR), UV–visible spectroscopy (UV–vis), and the electrical properties determined by Hall Effect Measurement. The application as a supercapacitor is also examined using Cyclic Voltammetry (CV), Charge–Discharge Cycling (GCD), and Electrochemical Impedance Spectroscopy (EIS). The resulting supercapacitor delivers an areal capacitance of \(3.39 mF{cm}^{-2}\) at a current density of 15.6 μA \({cm}^{-2}\) , making our synthesized graphene a good choice for electrochemical storage devices.
Graphene is a two-dimensional planar structure of s\({p}^{2}\) hybridized carbon atoms1 arranged in a honeycomb crystal lattice2 with an inter-layer spacing of \(\sim\) 3.35 Å. Graphite crystals, nanotubes, and fullerenes can be formed from graphene by stacking layers, rolling in a specific direction, or wrapping them into a ball3. Graphene is a unique nanomaterial with zero band gap4 and the only carbon allotrope where carbon atoms are tightly bonded to their neighbors by a unique electronic cloud deviating slightly from quantum mechanical principles5. These electrons move freely between the 2pz orbitals1, explaining why graphene exhibits unparalleled electrical conductivity5.
Graphene exhibits excellent electronic, mechanical, and thermal properties6. Graphene’s unique large surface area finds practical applications in energy storage, specifically batteries and supercapacitors7. Despite all these excellent properties and uses, the synthesis of high-quality, large-area graphene in a cost-effective way remains a significant challenge. Graphene was first isolated through mechanical exfoliation8, which has remained the typical conventional method of graphene synthesis8. Also, synthesis has been carried out via routes such as chemical exfoliation, chemical synthesis, thermal chemical vapor deposition, and unzipping carbon nanotubes9.
A significant drawback to the conventional graphene synthesis method involves using chemicals that are usually highly corrosive, explosive, and toxic10. The process’s cost of highly pure graphite remains another challenge11. Consequently, there is an attention shift to the synthesis of nanomaterials and graphene from natural sources12, most especially agro-waste13,14. Apart from easy availability and access to agro-waste, synthesis from agro-waste is straightforward, safe, and typically produces more stable materials15. They also offer an effective way of waste management13,16. Consequently, there has been the synthesis of nanomaterials and graphene from waste in general and agro-waste as well17,18 and used in electrochemical storage devices, wastewater treatment, and metal ion sensing, among others10. For example, graphene nanosheets were obtained by oxidizing graphite into graphene oxide using the Hummer method and highly concentrated acids, then using pomegranate juice as a reducing and capping agent to reduce graphene oxide19. Also, rice husk was combusted at 1123 K and chemically treated to obtain graphene sheets20. Furthermore, green tea-synthesized graphene sheets using a high-temperature pyrolysis technique have also been reported21. In all these works, graphene was obtained at elevated temperatures, and the synthesis process includes several steps, including chemical treatment.
Pomegranate peels constitute about 43% w/w of the entire fruit22 and are most readily available as waste, globally estimated to be 1.62 million tons22. The pomegranate peel contains a variety of bioactive substances, including hydrolyzable tannins, flavonoids, complex polysaccharides, and minerals, with gallic acid and punicalagin being the major phenolic compounds which makes them useful in many fields23. Although the peels have been utilized in synthesizing carbon dots for several applications24,25,26,27,28, the low-temperature synthesis of graphene from the pomegranate peel is yet to be reported.
Herein, we report on a one-pot synthesis of few-layered graphene sheets from a green and abundant precursor of pomegranate peel which was used solely to produce graphene, where no industrial chemicals were used in the synthesis process. The latter makes our method entirely green and energy efficient as the synthesis temperature does not exceed 80 °C. The morphology, microstructure, and electrical properties are determined, and the potential application as a supercapacitor is also examined.
Pomegranate fruit was sourced from a local market. The peel was removed and washed thoroughly with distilled water to remove the dust and impurities. The clean peels were subsequently dried in an oven at 40 °C overnight and blended into powder form using a blender.
The few-layered graphene sheets were synthesized via the hydrothermal method as follows:
A mass of 0.3 g of fine pomegranate peel powder was dissolved in 45 ml of distilled water and sonicated for 60 min. The solution was then transferred into a 750 ml Teflon-Line stainless steel autoclave and heated at 80 °C for 10 h. The solution was allowed to cool naturally, and filtration using a syringe and a 0.22 μm filter membrane was done for two turns. The solution was further filtered using a dialysis membrane against deionized water for 48 h. The resultant supernatant was stored at 4 °C for further use.
Quartz and FTO substrates were used in the studies for electrical measurements. In cleaning the substrates, firstly, the substrates were dipped in a solution of 2 ml of Hellmanex III and 200 ml of hot distilled water and sonicated for 10 min. The substrates were then rinsed thoroughly with distilled water. The substrates were further cleaned using an ozone cleaner for 10 min at a temperature of 24 °C. Thin film deposition of the few-layered graphene sheets was achieved by drop casting on the substrate and allowing it to air dry.
Electrochemical measurements were performed on specially designed electrodes fabricated by the Laser-Induced Graphene (LIG) technique. The LIG is a graphene synthesis technique that involves exposing a polymeric precursor to laser light to cause photochemical and thermal conversion into graphene29. One significant benefit of LIG is high conductivity30, a required condition for substrate selection in making electrodes for electrochemical measurements. Therefore, as part of this work, we also aim to examine the practicality of LIG as conducting substrates.
LIG electrode patterning was achieved in one step on a Kapton paper by using a high-powered \({CO}_{2}\) laser engraving machine (Versa LASER, VLS 3.50) of 10.6 µm wavelength, a voltage of 220 V, and a power of 5 W.
200 μl of the synthesized graphene was then drop-casted on LIG, which functioned as the conducting substrate for our synthesized graphene. After drying at room temperature for 48 h, a gel electrolyte layer was deposited, and the sample was dried for 6 h. Gel electrolyte was made by dissolving 5 g of PVA powder in 5 ml of \({H}_{2}{SO}_{4}\) and 45 ml of deionized water at \(90 ^\circ \mathrm{C}\) while stirring vigorously until a homogeneous solution was formed. After cooling, the solution was frozen at − 20 °C and thawed at 25 °C for 3 h to obtain the gel electrolyte. Measurements were made for LIG and the drop-casted sample on LIG (LIG + PG). PG refers to our synthesized graphene from pomegranate. The effectiveness of supercapacitors was then evaluated using Cyclic Voltammetry (CV), Galvanostatic Charge–Discharge (GCD), and Electrochemical Impedance Spectroscopy (EIS) with the VersaSTAT4 potentiostat.
The microstructure of the samples was studied using a high-resolution transmission electron microscope (TEM), JEM-2100F from JEOL Company, fortified with a 200 kV field emission gun. The elemental analysis was achieved by EDX, using an Oxford instrument 80 \({\mathrm{mm}}^{2}\) X-max detector system with point and ID mode. Raman Spectral analysis was conducted using the Micro Raman Confocal Microscope Witec Alpha300 model. Crystallinity and nature of synthesized GQDs were studied by an X-ray diffractometer 6100F from Shimadzu Company with a maximum power of 3 Kw, current of 30.0 mA, a divergent slit of 1.00 degree, scatter slit of 1.00, receiving slit of 0.3 mm with a scan range of 5–80 and a scan speed of 8 degrees per minute. The Fourier Transform Infrared spectra (FTIR) analysis was achieved using VERTEX 70v from Bruker Company with KBr as the reference. The optical structure was characterized by UV–Vis Spectroscopy using the Hitachi U-3900 UV spectrophotometer and a 10 mm path-length UV cell.
Experimental research and field studies on plants (either cultivated or wild), including the collection of plant material, must comply with relevant institutional, national, and international guidelines and legislation.
Figure 1a,b shows the TEM micrographs of the synthesized graphene at 80 °C with different magnifications. Based on the TEM analysis, the width of graphene lies in the range of ~ 100–400 nm with a lattice spacing of ~ 0.33 nm. Also, the inset of Fig. 1c shows a ring diffraction pattern, indicating some level of crystallinity of the synthesized graphene. High-resolution transmission electron microscope (HRTEM) images of the few-layered graphene sheets are shown in Fig. 1c,d. The HRTEM reveals the approximate number of layers of 2–4.
TEM micrographs of synthesized few-layered graphene sheets with different magnifications.
The elemental composition estimated by Energy dispersive X-Ray spectroscopy (EDX) is tabulated below. From Table 1, carbon is the majority, constituting 98.29% of the entire weight, and Oxygen, 1.71% weight. No extra elements apart from Carbon and Oxygen were observed, indicating high-quality synthesized graphene. The small number of oxygen molecules present could result from the oxidation of graphene due to its reaction with air.
Figure 2 shows the Raman spectra of the synthesized few-layered graphene sheets. Two peaks are observed at 1368.42 \({cm}^{-1}\) and 1564.42 \({cm}^{-1}\) . These values correspond to the D and G bands, respectively. The observed D band is due to disordered planes, and its intensity is prominent in few-layered graphene compared to single-sheet graphene. The D and G bands' intensity ratio (R) was 0.73, suggesting the excellent quality of the obtained few-layered graphene sheets31. For the 2D band, three peaks are observed at ~ 2834.42, 3087.70 \({cm}^{-1}\) and 3199.02 \({cm}^{-1}\) . The splitting of the 2D band into these three peaks results due to the double-resonance Raman process which involves phonon-electron scattering21. Also, the observed 2D band at 2834.42 cm–1 is blue-shifted due to the strain and vibrational phonons related to impurities32. On the other hand, the combinations of deconvoluted peaks at 3087.7 cm-1 and 3199.02 cm-1 can be ascribed to the D + G band33. The G to the 2D band ratio (i.e. IG/I2D) was also calculated to be 0.98, indicating layer numbers n < 534, which is consistent with that obtained from the HRTEM images.
Raman spectra of synthesized few-layered graphene sheets.
The XRD pattern of the synthesized few-layered graphene sheets is presented in Fig. 3. A broad diffraction peak centred at 2θ value of ~ 24° with a calculated d-spacing of 0.37 nm corresponding to the 002 planes of graphitic structures is observed35. The broad spectrum observed is due to the amorphous nature of the synthesized few-layered graphene sheets36, specifically, the disorder of graphite layers caused by empty rooms between graphite layers37. The broad peak is also observed due to the broadening of the d spacing21.
XRD spectrum of synthesized few-layered graphene sheets.
UV–vis spectra of the synthesized few-layered graphene were studied using the U-3900 spectrophotometer in the 200–800 nm wavelength range. As shown in Fig. 4, three peaks were observed at 214 nm, 256 nm, and 364 nm. The peak observed at 214 nm is assigned to sigma-sigma transitions, while the peak at 256 can be attributed to π-π* electronic transitions of s \({p}^{2}\) C=C bonds of the aromatic rings7,38, and the peak located at 364 nm is attributed to the n-π* transitions of the fewer C=O bonds present.
UV–visible spectrum of synthesized few-layered graphene sheets.
Figure 5 shows the FTIR spectra of the synthesized few-layered graphene sheets. From the spectra, a broad band is seen at 3,440.44 \({cm}^{-1}\) which is due to the stretching vibration of the –OH groups and the absorbed water molecules. The peaks observed at 2925.10 \({cm}^{-1}\) and 2853.79 \({cm}^{-1}\) arise from \(-{CH}_{2}\) stretching vibrations. The intense peak at 1637.31 \({cm}^{-1}\) is a result of the combination of COOH group stretching vibration and C=C skeletal vibrations from graphitic domains in the ketone or quinone groups. The weak peak observed at 1380.91 \({cm}^{-1}\) is due to the presence of C–O, and lastly, the observed peaks between 721.996 and 570.56 \({cm}^{-1}\) correspond to the bending of C-H39,40,41.
FTIR spectra of synthesized few-layered graphene sheets.
Oxygen functional groups on the surface of the synthesized few-layered graphene sheets make it hydrophilic, explaining its solubility in water.
To examine the electrical properties of the synthesized few-layered graphene sheets, Hall Effect measurements were conducted. Figure 6a–d shows the behavior of the few-layered graphene sheets under white light as the light intensity increases. Generally, the sheet concentration and sheet resistance increases with increasing intensity. In contrast, the electron mobility and conductivity decrease with increasing light intensity, indicating that our synthesized graphene sheets are light-sensitive and can find potential applications in optoelectronics.
Light intensity versus (a) sheet concentration, (b) Sheet resistance, (c) Mobility, and (d) Conductivity of synthesized few-layered graphene sheets.
The pomegranate peels consist mainly of hydrolyzable punicalagin, a bioactive compound with a chemical structure including gallagic acid and ellagic acid connected through a glucose molecule. This compound has a common feature, the presence of labile oxygen linkages, responsible for the cyclization and metamorphosis of the punicalagin molecules. Most likely, the heating temperature at 80 °C and the pressure inside the autoclave are capable of hydrolyzing punicalagin and breaking these labile oxygen linkages resulting in the release of ellagic acid. Therefore the reaction proceeds by the breaking of the labile bonds, followed by the release of \({H}_{2}O\) and then the subsequent aromatization leading eventually to the formation of few-layered graphene sheets. The schematic diagram for few-layered graphene sheet formation is shown in Fig. 7.
Schematics for forming few-layered graphene sheets from pomegranate peel.
Cyclic voltammetry was performed for the LIG Fig. 8 and the synthesized few-layered graphene (PG) on LIG substrate (LIG + PG). The behavior of both electrodes was investigated within the same potential window of (0–0.9)V and at scan rates in the range of 10–100 m \({Vs}^{-1}\) . As shown in Fig. 9a, the obtained curves for both samples show rectangular curves, which are typical of an Electric Double Layer Capacitor (EDCL)42. Rectangular-shaped CV curve also indicates low contact resistance and ideal charge propagation of the electrodes43.
A digital photograph of LIG electrode pattern on Kapton paper.
(a) Comparative CV profiles of LIG and LIG + PG at 20 mV \({s}^{-1}\) . CV at different scan rates for (b) LIG and (c) LIG + PG. (d) Change in areal specific capacitance at different scan rates for LIG and LIG + PG.
Comparatively, LIG + PG has a larger CV area, indicating higher capacitance and better rate capability. Also, from Fig. 9b and c, it can be seen that the curves of both samples are more rectangular at lower scan rates than that at higher scan rates. This is because higher scan rates usually generate considerable Ohmic resistance, effectively distorting the CV loop and narrowing the loop with an oblique angle44. A plot of the Capacitance versus the Scan rates is shown in Fig. 9d. From the graph, it is evident that the capacitance of both samples decreases as the scanning rate increases. This result is expected of carbon-based materials because of the limited transfer of ions to the carbon particle surface, which results in areas of the electrode layer not being accessible at high scan rates43. Also, at low scan rates, a more homogeneous potential with minimal variations is created along the material45. The specific areal capacitance at 20 m \({Vs}^{-1}\) for LIG is 0.29 mF \({cm}^{-2}\) and LIG + PG is 1.22 mF \({cm}^{-2}\) with the effective specific areal capacitance, i.e. the specific areal capacitance from our synthesized graphene, being 0.93 mF \({cm}^{-2}\) which is comparatively higher than some reported works46.
The GCD behavior of the samples was studied at various current densities within the range of 10–50 μA \({cm}^{-2}\) as shown in Fig. 10b and c. Generally, as the current density increases, the effective area decreases. Figure 10a shows the comparative GCD curve at a current density of 26 μA \({cm}^{-2}.\) As seen, the LIG + PG exhibits a longer charging and discharge than the LIG, and this is an indication of higher capacitance for the former.
(a) Comparative GCD curves for LIG (in red) and LIG + PG (in black). (b) GCD curves for LIG at different current densities (c) GCD curves for LIG + PG at different current densities (d) Areal specific capacitance versus current density of both samples: LIG (in red), LIG + PG (in black).
A sharp voltage drop is observed at the beginning of discharge for both samples, which is due to the diffusion-limited mobility of the electrolyte ions in the electrode pores and could result from the interface resistance between the current collector and the active layer or the conductivity of highly porous activated carbon45. Voltage drop for LIG was found to be 0.11 V, and that of LIG + PG was found to be 0.082 V, with the difference equating to 0.028 V. This indicates that our synthesized few-layered graphene sheets contributed a relatively small amount, almost negligible, to the voltage drop.
A plot of the areal specific capacitance versus current density is shown in Fig. 10d. The areal specific capacitance values decrease as the current densities increase. The equation \({C}_{A}\) = \(\frac{I\Delta t }{{A}_{act}\Delta V}\) , was used in calculating the areal specific capacitance (areal) for both samples at different current densities. As expected, the LIG + PG had relatively high areal specific capacitance values. At 15.6 μA \({cm}^{-2},\) the areal specific capacitance for LIG and LIG + PG was 0.66 mF \({cm}^{-2}\) and 3.99 mF \({cm}^{-2}\) respectively with the effective capacitance having a value of 3.39 mF \({cm}^{-2}\) , comparatively higher than previously reported works47 and thus indicating good capacitor behavior of our synthesized graphene. A summary of the electrochemical performance of the sample can be found in Table 2.
EIS was further used to characterize the performance of the graphene samples. The experiment was performed in the frequency range of 100 MHz to 0.1 Hz. Figure 11a shows the Nyquist plots obtained from the EIS data. The Nyquist plots obtained consists of a straight line segment with a slope of 45° followed by another line with a steeper slope as expected of electric double-layer capacitors. Also, the absence of a semi-circle further confirms the EDCL behavior42, corroborating the results obtained in the CV measurements.
(a) Nyquist plot of LIG (in black) and LIG + PG (in red) in the frequency range 100 MHz–0.1 Hz (b) Nyquist plot with fitting and an equivalent circuit model (inset) of LIG (c) Nyquist plot with fitting and an equivalent circuit model (inset) of LIG + PG.
EIS plot fitting was done using the EIS Spectrum Analyzer to get the equivalent circuit model of the EIS plot, shown in Fig. 11b and c. The first part of the equivalent circuit gives information about the equivalent series resistance (\({R}_{ESR})\) . \({R}_{ESR}\) for LIG was found to be 495.17 Ω and that of LIG + PG was found to be 859.47 Ω. Additionally, the second component of the circuit is a parallel assembly of the constant phase element (CPE 1), Warburg impedance (Wo), and charge transfer resistance (Rct), which represents the charge transfer phenomenon of porous graphene electrodes46. The charge transfer resistance (\({R}_{ct})\) for LIG was 25.61 Ω and that of LIG + PG was 33.09 Ω. The lower values of \({R}_{ct}\) signifies lower ionic transfer resistance effect within the smaller pores inside the electrode active sites46. Our synthesized graphene's relatively lower resistant values make it an excellent choice for energy storage since lower resistant values are necessary for minimizing supercapacitor losses and increasing overall efficiency.
In summary, we have successfully developed for the first time a green, facile, and energy-efficient method of synthesizing few-layered graphene sheet from pomegranate peels via the hydrothermal method at a low temperature of 80 °C without the aid of any passivating agent. The microstructure, morphology, and electrical properties studies show that our synthesized graphene is of high quality. Excellent electrochemical performance has also been achieved with the areal capacitance of 3.39 mF \({cm}^{-2}\) at a current density of 15.6 μA \({cm}^{-2}\) , making our synthesized graphene applicable as a supercapacitor for energy storage.
The datasets used and/or analyzed during the current study are available from the corresponding author upon reasonable request.
Perez, M. C., Angel, M., Hernandez, V. & Elias, J. "Hybridization bond states and band structure of graphene: A simple approach. Eur. J. Phys. https://doi.org/10.1088/1361-6404/ac654e (2022).
Hu, T. et al. Synthesis of few-layer graphene sheets from waste expanded polystyrene by dense Fe cluster catalysis. ACS Omega 5(8), 4075–4082. https://doi.org/10.1021/acsomega.9b03743 (2020).
Article CAS PubMed PubMed Central Google Scholar
Güçlü, AD, Potasz, P., Korkusinski, M. & Hawrylak, P. GrapheneQuantumDots (Springer-Verlag Berlin Heidelberg, 2014).
Tiwari, S. K., Mishra, K., Ha, K. & Huczko, A. Evolution of graphene oxide and graphene: From imagination to industrialization. ChemNanoMat https://doi.org/10.1002/cnma.201800089 (2018).
Tiwari, S. K., Sahoo, S., Wang, N. & Huczko, A. Graphene research and their outputs: Status and prospect. J. Sci. Adv. Mater. Devices 5(1), 10–29. https://doi.org/10.1016/j.jsamd.2020.01.006 (2020).
Luo, Z., Lu, Y., Somers, L. A. & Johnson, A. T. C. High yield preparation of macroscopic graphene oxide membranes. J. Am. Chem. Soc. 131, 898–899 (2009).
Article CAS PubMed Google Scholar
Mbayachi, V. B. et al. Graphene synthesis, characterization and its applications: A review. Results Chem. 3, 100163. https://doi.org/10.1016/j.rechem.2021.100163 (2021).
Fatihah, N., Arifin, T., Yusof, N., Fauzi, A. & Jaafar, J. Graphene from waste and bioprecursors synthesis method and its application: A review. Malays. J. Fund. Appl. Sci 16(3), 342–350 (2020).
Bhuyan, M. S. A., Uddin, M. N., Islam, M. M., Bipasha, F. A. & Hossain, S. S. Synthesis of graphene. Int. Nano Lett. 6(2), 65–83. https://doi.org/10.1007/s40089-015-0176-1 (2016).
Torres, F. G., Troncoso, O. P., Rodriguez, L. & De-la-Torre, G. E. Sustainable synthesis, reduction and applications of graphene obtained from renewable resources. Sustain. Mater. Technol. 29, e00310. https://doi.org/10.1016/j.susmat.2021.e00310 (2021).
Akhavan, O., Bijanzad, K. & Mirsepah, A. Synthesis of graphene from natural and industrial carbonaceous wastes. RSC Adv. https://doi.org/10.1039/c4ra01550a (2014).
Ahmed, H. M., Ghali, M., Zahra, W. & Ayad, M. M. Preparation of carbon quantum dots/polyaniline nanocomposite: Towards highly sensitive detection of picric acid. Spectrochim. Acta A Mol. Biomol. Spectrosc. 260, 119967. https://doi.org/10.1016/j.saa.2021.119967 (2021).
Article ADS CAS PubMed Google Scholar
Nath, P. C. et al. Biogeneration of valuable nanomaterials from agro-wastes: A comprehensive review. Agronomy https://doi.org/10.3390/agronomy13020561 (2023).
Huston, M., DeBella, M., DiBella, M. & Gupta, A. Green synthesis of nanomaterials. Nanomaterials 11, 2130. https://doi.org/10.3390/nano11082130Academic (2021).
Article CAS PubMed PubMed Central Google Scholar
Dutta, V. et al. Bio-inspired synthesis of carbon-based nanomaterials and their potential environmental applications: A state-of-the-art review. Inorganics https://doi.org/10.3390/inorganics10100169 (2022).
Devadiga, A. & Shetty, K. V. Timber industry waste-teak (Tectona grandis Linn.) leaf extract mediated synthesis of antibacterial silver nanoparticles. Int. Nano Lett. 5(4), 205–214. https://doi.org/10.1007/s40089-015-0157-4 (2015).
Adelere, I. A. & Lateef, A. "A novel approach to the green synthesis of metallic nanoparticles : the use of agro-wastes, enzymes, and pigments. Nanotechnology Reviews 5(6), 567–587. https://doi.org/10.1515/ntrev-2016-0024 (2016).
Ruan, G., Sun, Z., Peng, Z. & Tour, J. M. Growth of graphene from food, insects, and waste. ACS Nano 5(9), 7601–7607. https://doi.org/10.1021/nn202625c (2011).
Article CAS PubMed Google Scholar
Tavakoli, F., Salavati-niasari, M. & Mohandes, F. Green synthesis and characterization of graphene nanosheets. Mater. Res. Bull. 63, 51–57. https://doi.org/10.1016/j.materresbull.2014.11.045 (2015).
Muramatsu, H. et al. Rice husk-derived graphene with nano-sized domains and clean edges. Small 10(14), 2766–2770. https://doi.org/10.1002/smll.201400017 (2014).
Article CAS PubMed Google Scholar
Roy, A., Kar, S., Ghosal, R., Naskar, K. & Bhowmick, A. K. Facile synthesis and characterization of few-layer multifunctional graphene from sustainable precursors by controlled pyrolysis, understanding of the graphitization pathway, and its potential application in polymer nanocomposites. ACS Omega 6(3), 1809–1822. https://doi.org/10.1021/acsomega.0c03550 (2021).
Article CAS PubMed PubMed Central Google Scholar
Ko, K., Dadmohammadi, Y. & Abbaspourrad, A. Nutritional and bioactive components of pomegranate waste used in food and cosmetic applications: A review. Foods 10(3), 657. https://doi.org/10.3390/foods10030657 (2021).
Article CAS PubMed PubMed Central Google Scholar
Charalampia, D. & Koutelidakis, A. Ε. From pomegranate processing by-products to innovative value added functional ingredients and bio-based products with several applications in food sector. BAOJ Biotech 3(1), 210 (2017).
Muktha, H. et al. Green synthesis of carbon dots and evaluation of its pharmacological activities. Bionanoscience 10(3), 731–744. https://doi.org/10.1007/s12668-020-00741-1 (2020).
Asadollahzadeh, H., Ghazizadeh, M. & Manzari, M. Developing a magnetic nanocomposite adsorbent based on carbon quantum dots prepared from Pomegranate peel for the removal of Pb(II) and Cd(II) ions from aqueous solution. Anal. Methods Environ. Chem. J. 4(03), 33–46. https://doi.org/10.24200/amecj.v4.i03.149 (2021).
Vyas, Y., Chundawat, P., Dharmendra, V., Punjabi, P. B. & Ameta, C. Green and facile synthesis of luminescent CQDs from pomegranate peels and its utilization in the degradation of azure B and amido black 10B by decorating it on CuO nanorods. ChemistrySelect 6(33), 8566–8580. https://doi.org/10.1002/slct.202102156 (2021).
Qureshi, W. A. et al. Antimicrobial activity and characterization of pomegranate peel-based carbon dots. J. Nanomater. https://doi.org/10.1155/2021/9096838 (2021).
Anagbonu, P., Allam, A. & Ghali, M. Low temperature synthesis of fluorescent carbon dots from pomegranate peels. Key Eng. Mater. 931, 25–31. https://doi.org/10.4028/p-14439u (2022).
Vivaldi, F. M. et al. Three-dimensional (3D) laser-induced graphene: Structure, properties, and application to chemical sensing. ACS Appl. Mater. Interfaces https://doi.org/10.1021/acsami.1c05614 (2021).
Article PubMed PubMed Central Google Scholar
Beduk, T., Lahcen, A. A., Tashkandi, N. & Salama, K. N. Sensors and actuators B: Chemical one-step electrosynthesized molecularly imprinted polymer on laser scribed graphene bisphenol a sensor. Sens. Actuators B Chem. 314, 128026. https://doi.org/10.1016/j.snb.2020.128026 (2020).
Subrahmanyam, K. S., Vivekchand, S. R. C., Govindaraj, A. & Rao, C. N. R. A study of graphenes prepared by different methods: Characterization, properties and solubilization. J. Mater. Chem. https://doi.org/10.1039/b716536f (2008).
Hähnlein, B. et al. Investigation of epitaxial graphene via Raman spectroscopy: Origins of phonon mode asymmetries and line width deviations. Carbon 170, 666–676. https://doi.org/10.1016/j.carbon.2020.07.016 (2020).
Pimenta, M. A., Dresselhaus, G., Dresselhaus, M. S. & Canc, L. G. Studying disorder in graphite-based systems by Raman spectroscopy. Phys. Chem. Chem. Phys. https://doi.org/10.1039/b613962k (2007).
Singh, M., Jha, H. S. & Agarwal, P. Growth of large sp2 domain size single and multi-layer graphene films at low substrate temperature using hot filament chemical vapor deposition. Mater. Lett. 126, 249–252. https://doi.org/10.1016/j.matlet.2014.04.066 (2014).
Chinnadurai, D., Karuppiah, P., Chen, S., Kim, H. & Prabakar, K. Metal-free multiporous carbon for electrochemical energy storage and electrocatalysis applications. New J. Chem. https://doi.org/10.1039/C9NJ01875A (2019).
Singhbabu, Y. N., Didwal, P. N., Jang, K. & Jang, J. Green synthesis of a reduced-graphene-oxide wrapped nickel oxide nano-composite as an anode for high- performance lithium-ion batteries. ChemistrySelect https://doi.org/10.1002/slct.202200676 (2022).
Ruaysap, M., Pongphai, T., Sirilapphokhin, K., Sirilapphokhin, P. & Tipparach, U. Synthesis of graphene from food and agricultural wastes in ubon ratchathani province, Thailand. J. Mater. Sci. Appl. Energy 11(2), 244465. https://doi.org/10.55674/jmsae.v11i2.244465 (2022).
Johra, F. T., Lee, J. W. & Jung, W. G. Facile and safe graphene preparation on solution based platform. J. Ind. Eng. Chem. 20(5), 2883–2887. https://doi.org/10.1016/j.jiec.2013.11.022 (2014).
Ramya, A. V., Manoj, B. & Mohan, A. N. Extraction and characterization of wrinkled graphene nanolayers from commercial graphite. Asian J. Chem. 28(5), 1031–1034. https://doi.org/10.14233/ajchem.2016.19577 (2016).
Matulková, I., Kovaříček, P., Šlouf, M., Němec, I. & Kalbáč, M. Surface enhanced infrared absorption spectroscopy for graphene functionalization on copper.Carbon 124, 250–255.https://doi.org/10.1016/j.carbon.2017.08.045 (2017).
Surekha, G., Krishnaiah, K. V., Ravi, N. & Padma Suvarna, R. FTIR, Raman and XRD analysis of graphene oxide films prepared by modified Hummers method. J. Phys. Conf. Ser. https://doi.org/10.1088/1742-6596/1495/1/012012 (2020).
Mathis, T. S. et al. Energy storage data reporting in perspective—Guidelines for interpreting the performance of electrochemical energy storage systems. Adv. Energy Mater. 9(39), 1–13. https://doi.org/10.1002/aenm.201902007 (2019).
Rasenthiram, L. Synthesis of graphene fibers for use in supercapacitors (2015).
Cheng, L. et al. Electrocapacitive properties of supercapacitors based on hierarchical porous carbons from chestnut shell. Coll. Surf. A Physicochem. Eng. Asp. 446, 127–133. https://doi.org/10.1016/j.colsurfa.2014.01.057 (2014).
Ramirez, N. et al. Capacitive behavior of activated carbons obtained from coffee husk. RSC Adv. 10(62), 38097–38106. https://doi.org/10.1039/d0ra06206e (2020).
Article ADS CAS PubMed PubMed Central Google Scholar
Ray, A., Roth, J. & Saruhan, B. Structured graphene electrodes based flexible micro-supercapacitor for efficient peak energy storage. Molecules 27, 329 (2022).
Article CAS PubMed PubMed Central Google Scholar
Pham, T. V. et al. High areal capacitance of N-doped graphene synthesized by arc discharge. Adv. Funct. Mater. 29(48), 1–9. https://doi.org/10.1002/adfm.201905511 (2019).
P. A acknowledges JICA through the TICAD7 Scholarship. The authors appreciate the Graphene Center of Excellence for Electronic and Energy Applications and the lab engineers of TMD, E-JUST, for their contribution. The work was supported by project 38311 from the STDF agency in Egypt.
Open access funding provided by The Science, Technology & Innovation Funding Authority (STDF) in cooperation with The Egyptian Knowledge Bank (EKB).
Basic and Applied Sciences Institute, Egypt-Japan University of Science and Technology, New Borg El-Arab, 21934, Alexandria, Egypt
Prince Anagbonu & Mohsen Ghali
Physics Department, Faculty of Science, Kafrelsheikh University, Kafrelsheikh, Egypt
Department of Electronics and Communications Engineering, Faculty of Engineering, Egypt-Japan University of Science and Technology, New Borg El-Arab, 21934, Alexandria, Egypt
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
You can also search for this author in PubMed Google Scholar
P.A: Conceptualization, methodology, writing & editing. M.G.: Conceptualization, methodology, review, and editing. A.A.: Review and editing. Project supervisor: M.G.
The authors declare no competing interests.
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
Anagbonu, P., Ghali, M. & Allam, A. Low-temperature green synthesis of few-layered graphene sheets from pomegranate peels for supercapacitor applications. Sci Rep 13, 15627 (2023). https://doi.org/10.1038/s41598-023-42029-w
DOI: https://doi.org/10.1038/s41598-023-42029-w
Anyone you share the following link with will be able to read this content:
Sorry, a shareable link is not currently available for this article.
Provided by the Springer Nature SharedIt content-sharing initiative
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.
Scientific Reports (Sci Rep) ISSN 2045-2322 (online)
Ultra Capacitor Sign up for the Nature Briefing newsletter — what matters in science, free to your inbox daily.